  Synthetic rubbers
 

Application: 		The rubbers of the general purposes used for
                        the production of tires and different rubber 
                        goods replacing natural rubber in production 
                        of medical articles, colored rubber shoes, 
			rubber articles for the food industry etc. 
                        Perfectly combined with other types of 
                        rubbers ( SKD, BSK etc. )

BK - 1675

Mooney viscosity MB 1 - 8 ( 125 C )
Mooney viscosity spread inside a batch, max.
Insaturation, % mol.
Ash content, % max.
Weight loss at drying, % max.
Antioxidant content, %
Agidol - 2
or Irganox 1010
46-56
8
1.40 - 1.80
0.4
0.3

0.05-0.20
0.02 - 0.08

Packing			in 30 +/- 1 kg briquettes wrapped up in PE 
                        film put into 1 MT wooden crates or containers.
Loading capacity	23.6 MT net per 40` FCL
Country Of Origin	Russian Federation

SKI-3, SKI-3S

Property
Mooney Viscosity MB 1 - 4 at 100 C
Mooney viscosity spread inside the batch, max.
Ash content , % max.
Weight loss at drying, % max.
Antioxidant content, %
DFFD
or VTS
or Diaphen 13
or NQ-2246 ( Agidol - 2 )
SKI-3
65 - 85
+/-4
0.5
0.6

0.15 - 0.3
0.4 - 0.7
0.3 - 0.5
-
SKI-3S
61 - 84
+/-4
0.35
1.2

-
-
-
0.2 - 0.6

SBR-1502

Mooney viscosity MB 1 - 4 ( 100 C )
Mooney viscosity spread inside a batch, % max.
Tensile strength, MPa min.
Elongation at break, % min.
Rebound elasticity, % min.
Ash content, % max.
Weight loss at drying, % max.
Antioxidant content, %
Mass fraction of Cu, % max.
Mass fraction of Fe, % max.
Mass fraction of organic acids, %
Mass fraction of organic acids soaps, % max.
Mass fraction of bound Styrene, %
48-58
5
27
560
38
0.8
0.4
1 - 2
0.000015
0.004
5.2 - 7.2
0.25
22 - 25

Packing			in 30 +/- 1 kg briquettes wrapped up in PE 
                        film put into 450 kg net crates
Loading capacity	23.6 MT net per 40` FCL
Country Of Origin	Russian Federation

SKD-2 (BR-1220)

Mooney viscosity MB 1 - 4 ( 100 C )
Mooney viscosity spread inside a batch, % max.
Mass fraction of CIS-1,4 units, %
Tensile strength, MPa min.
Elongation at break, % min.
Modulus at 300 % elongation, MPa min.
Residual deformation after break, % max.
Rebound elasticity, % min.
Ash content, % max.
Weight loss at drying, % max.
Antioxidant Agidol - 2 content, %
Mass fraction of Cu, % max.
Mass fraction of Fe, % max.
40 - 50
6
87 - 90
19.1
480
19.1
12
51
0.3
0.3
0.05 - 0.20
0.0002
0.0004
Packing			in 30 +/- 1 kg briquettes wrapped up in PE 
                        film put into 1 MT wooden crates or containers.
Loading capacity	23.6 MT net per 40` FCL
Country Of Origin	Russian Federation

SKN-26M

Mooney viscosity MB 1 - 4 ( 100 C )
Mooney viscosity spread inside a batch, max.
Hardness, N
Tensile strenght, MPa min.
Elongation at break, % min.
Vulcanizate mass variation in Isooctantoluene, %max.
Ash content, % max.
Weight loss at drying, % max.
Antioxidant content, %
- Diaphene
- Agidol
Mass fraction of Cu, % max.
Mass fraction of Fe, % max.
Mass fraction of organic acids, %
Mass fraction of organic acids soaps, % max.
Mass fraction of bound Nitrile of Acrylic Acid, %
48 - 58 / 70 - 90
5
5.8 - 8.3 /17.2 - 21.5
27.5
625
34
0.6
1

0.2 - 0.3
0.05 - 0.10
0.000015
0.004
6.5
0.4
27 - 30
Packing			in 30 +/- 1 kg briquettes wrapped up in PE 
                        film put into 450 kg net crates.
Loading capacity	23.6 MT net per 40` FCL
                        43.2 MT net per r/r box-car
Country Of Origin	Russian Federation